question : find intrinsic carrier concentration at T=200k for silicon (in cm^-3).
Answer is attached.In that why is that (200/300)^3 is added there.my only hope is this forum.Thank you
question : find intrinsic carrier concentration at T=200k for silicon (in cm^-3).
Answer is attached.In that why is that (200/300)^3 is added there.my only hope is this forum.Thank you
For some reason, the answer I gave to this problem, and answers others gave to your other threads seemed to disappear last night. Perhaps the keepers this forum can shed some light on this event.
For some reason, the answer I gave to this problem, and answers others gave to your other threads seemed to disappear last night. Perhaps the keepers this forum can shed some light on this event.
From my view as a moderator I can see where posts have been deleted.
There are no visibly deleted posts in this or other threads by bhuvaneshnick.
I can only suggest that either the forum had some kind of major software fart resulting in the post not sticking or getting lost, or you are confusing the posts here on ETO with the OPs identical posts on AAC or any other forum.
From my view as a moderator I can see where posts have been deleted.
There are no visibly deleted posts in this or other threads by bhuvaneshnick.
I can only suggest that either the forum had some kind of major software fart resulting in the post not sticking or getting lost, or you are confusing the posts here on ETO with the OPs identical posts on AAC or any other forum.
The last explanation is correct. The OP has posted this problem to at least two different places that I am aware. I guess he wants a consensus of of opinion to determine the answer. My apologies for the confusion. I should have noticed the multiple postings earlier.